Starc Metals is a reputable manufacturer and supplier located in Canberra, Australia, focusing on high-quality Stainless Steel Bright Bars and Rods. Renowned for our precision engineering and top-notch finishing, we strictly adhere to international standards, ensuring our products are not only strong and durable but also visually appealing. Our bright bars and rods boast a sleek, polished surface, thanks to advanced finishing techniques that provide outstanding corrosion resistance and mechanical performance. With a commitment to rigorous quality control and modern manufacturing methods, Starc Metals delivers reliable, high-performance materials ideal for various industries, including automotive, aerospace, chemical processing, construction, and food processing, all while ensuring both functionality and aesthetic excellence.
Stainless Steel Bright Bars and Rods are primarily made from iron, chromium, and nickel, with specific amounts of carbon, molybdenum, and other alloying elements tailored to each grade. They offer remarkable corrosion resistance, high tensile and yield strength, and excellent toughness. The bright finish not only enhances surface smoothness but also reduces friction and boosts wear resistance. With impressive ductility, hardness, and fatigue strength, these bars and rods maintain their mechanical integrity even under heavy loads, high temperatures, and harsh chemical environments, making them perfect for critical applications that demand both performance and a high-quality surface finish.
Standards : ASTM A276, ASTM A484, AISI
Grade : 201, 202, 301, 302, 303, 304, 304H, 304L, 316, 316H, 316L, 309, 309S, 310, 310S, 316Ti, 317, 317L, 347, 321, 321H, 410, 416, 420, 430, 430F, 431, 440C, 630, 17-4PH, F51
Range : from2.00mm to 6.35mm (0.078″ to 0.25″)dia.
Tolerance : DIN 671, ASTM A484 & as per customer’s specific requirement.
Finish : Cold drawn, Centreless Ground, Polished
| Grade | Su | C | Si | P | Cr | Ni | M | Mo | Other |
|---|---|---|---|---|---|---|---|---|---|
| 316 | 0.030 max | 0.08 max | 0.75 max | 0.045 max | 16.0-18.0 | 10.0 14.0 | 2.00 max | 2.0 3.0 | – |
| 317L | 0.030 max | 0.035 max | 0.75 max | 0.045 max | 18.0-20.0 | 11.0 14.0 | 2.00 max | 3.0 4.0 | – |
| 304 | 0.030 max | 0.08 max | 0.75 max | 0.045 max | 18.0-20.0 | 8.0 11.0 | 2.00 max | – | – |
| 310 S | 0.030 max | 0.08 max | 1.5 max | 0.045 max | 24.0-26.0 | 19.0 22.0 | 2.00 max | 3.0 4.0 | – |
| 347 H | 0.030 max | 0.04 0.10 | 0.75 max | 0.045 max | 17.0- 19.0 | 9.0 13.0 | 2.00 max | – | 10C(Cb+Ta)<1.10% |
| 321 | 0.030 max | 0.08 | 0.75 max | 0.045 max | 17.0-20.0 | 9.0 12.0 | 2.00 max | – | 5C 0.70% |
| Grade | Tensile Strength | Yield Strength (0.2%Offset) | Density | Elongation | Melting Point |
|---|---|---|---|---|---|
| SS 303 | Psi – 85,000 | Psi – 45,000 | 55% | 50 % | Rb 180 |
| SS 202 | 515 MPa | 275 MPa | 8.0 g/cm3 | 40 % | 1454 °C |
| SS 304 | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 40% | 1400 °C |
| SS 304L | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 40% | 1400 °C |
| SS 316 | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 35 % | 1454 °C |
| SS 316L | 485 Min | 170 Min. | 8.0 g/cm3 | 40 % | 1400 °C |
|
Drawn Bar |
Min. (mm) |
Max. (mm) |
Drawn Bar |
Min. (inch) |
Max. (inch) |
|---|---|---|---|---|---|
|
Rounds |
14 mm |
76 mm |
Rounds |
5/8” |
3” |
|
Flats Width :
Height : |
20 mm
5mm |
100 mm
40 mm |
Flats Width :
Height : |
3/4″
1/2″ |
4”
1-1/2” |
|
Squares |
14 mm |
65 mm |
Squares |
1/2″ |
2-1/2” |
|
Hexagonals |
12 mm |
60 mm |
Hexagonals |
5/8” |
2” |
|
Bright Bar Weight Calculation Formula |
|
|
Bright Bar Weight Formula
0.00623 X ( mm ) Diam X ( mm ) Diam = Weight / Meter
0.0019 X ( mm ) Diam X ( mm ) Diam = Weight / Feet |
Square Bar Weight Formula0.00788 X ( mm ) Diam X ( mm ) Diam = Weight / Meter
0.00240 X ( mm ) Diam X ( mm ) Diam = Weight / Feet
|
|
Brightagonal Bar Weight Forumla
0.00680 X ( mm ) Diam X ( mm ) Diam = Weight / Meter
0.002072 X ( mm ) Width X ( mm ) Diam = Weight / Feet |
Bright Bar Weight Forumla
0.00798 X ( mm ) Thickness X ( mm ) Width = Weight / Meter
0.00243 X ( mm ) Width X ( mm ) Thickness = Weight / Feet |
Yes, stainless steel bright bars and rods can be customized in size according to specific requirements. They are available in various diameters, lengths, and finishes to suit diverse industrial applications.
Yes, stainless steel bright bars are highly corrosion-resistant due to their chromium content, which forms a protective oxide layer, preventing rust and ensuring durability in various harsh environments and applications.
Yes, stainless steel bright bars can be welded. They are compatible with various welding methods, including TIG, MIG, and stick welding. However, proper precautions, such as controlling heat input, are needed to maintain corrosion resistance and prevent distortion.
These Stainless Steel Bright Bars and Rods find extensive use in industries that prioritize durability, corrosion resistance, and a polished surface. In automotive and aerospace sectors, they serve as shafts, fasteners, and precision components. The chemical and petrochemical industries rely on them for valves, pumps, and reactors that face corrosive conditions. In the food processing and pharmaceutical fields, bright bars and rods are essential for hygienic equipment, storage tanks, and machinery, thanks to their smooth, easy-to-clean surfaces.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Starc Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Canberra, Australia
Copyright 2024 Starc Metals. All rights reserved